Metaflux 70-45 Cutting-Spray detergent liquid
Zinc Spray 70-45
Cold galvanized spray, are at room temperature surface treatment, different from the hot galvanized, but with the same hot cathode galvanized anti-rust effect.
Zinc spray is a major technological breakthrough for the Metaflux Swiss plant in 1975. For the first time in the world, high-purity, high-content, ultra-small particles of zinc are sprayed through aerosol cans to form metallic and cathodic zinc Layer, and obtained a patent certificate.
- 描述
- Global Tab
描述
Zinc Spray 70-45
Cold galvanized spray, are at room temperature surface treatment, different from the hot galvanized, but with the same hot cathode galvanized anti-rust effect.
Zinc spray is a major technological breakthrough for the Metaflux Swiss plant in 1975. For the first time in the world, high-purity, high-content, ultra-small particles of zinc are sprayed through aerosol cans to form metallic and cathodic zinc Layer, and obtained a patent certificate.
Products in accordance with DIN50976 (1980) European anti-corrosion standards, excellent adhesion, can replace the hot galvanized for bare metal surface, the formation of anti-corrosion zinc coating; can also be used for the repair of galvanized parts, such as cutting surface, Make hot galvanized repair parts. Under normal conditions of use, the anti-corrosion time in the atmosphere up to twenty years or more. And the market on the ordinary zinc powder paint has a bad day.
Get free sample or more information , please contact me with my email: jenny@fuji-hk.cn . thank you .
相关产品
-
Metaflux 79-06 Porcelain cold galvanized spray magic oil sex spray
Potter Zinc Spray 79-06
“Cold galvanized spray” is the surface temperature treatment, unlike hot galvanized, but has the same effect of hot galvanizing rust.
Zinc spray is a major technological breakthrough for the 1975 Metaflux Swiss plant. For the first time in the world, high purity, high content, ultra-small size zinc spray through the aerosol cans to form metal and cathode zinc layer, and obtain a patent certificat
-
supply Metaflux 70-34 rust protection agent spray paint protective film
70-34 rust protection agent technical parameters
Use range
Vehicles, trucks, engineering vehicles, other machinery and equipment of the anti-corrosion maintenance;
A variety of metal structures on-site anti-corrosion maintenance;
Ship, rail industry, anti-corrosion maintenance.
Instructions
Before brushing, the need to remove the surface of the dust, oil, grease, wax, silicon and other dirt; can be used in the corrosion of the metal surface, need to remove the rust can be (st2 rust level).
Precautions
For outdoor use, you need another brush finish to prevent the coating from aging.
All coatings can be used as topcoats, overcoats, and are recommended for trial compatibility, especially coatings with high solvent content or aggressive solvents.
-
Metaflux 70-37 rust safety anti rust lubricant oil spray
Use range
1. Automobile manufacturing (maintenance of cars, trucks and other fuselages)
2. Construction (repair of steel structure), maintenance of ships and railways.
Instructions
1. Before use, shake the tank sufficiently
2. Before spraying, remove the surface of the material oil or grease. First rusty rust, rust to remove
3. Spraying distance of at least 25cm (10 inches) or more 8.53 / 30
4. To prevent aging, the coating surface should be re-painted
-
METAFLUX 70-05scale inhibitor corrosion inhibitor
Product Description: The 70-05 series is a special rust-removing solvent for fastened stuck bolts. It is an efficient “liquid wrench” that can penetrate into oil, grease and carbonized oil. A few minutes will be able to loosen a variety of serious corrosion or stuck bolt parts, and can quickly remove the various due to freezing shrinkage, corrosion and burr caused by the phenomenon of screw stuck. Product viscosity below water and penetration is stronger than the traditional stripping oil, does not contain any acidic substances (especially phosphoric acid), does not contain any grease or oily substances, the composition of non-toxic side effects. Through the cooling shrinkage to rust the loose bolts, the treated place 10 to 15 minutes after the automatic decomposition, will not produce fisheye effect. The treated surface can be sprayed after 15 minutes
-
Metaflux 70-40 zinc thermal lead polishing Zinc paste
product manual:
Gray epoxy, suitable for long-term protection of metal surfaces. Manufactured in accordance with European specifications DIN50.976 / 1980. Zinc powder purity of 98.5% to 99%, surface dry zinc content of 96%. Can be reliably adhered to all metal surface .20 ℃ after 10 minutes after the hand touch, the full curing time of 80 ℃ for 24 hours; outer drying time of 20 ℃ 60 to 120 minutes. Dry after the cracks will not produce a brushing thickness of 150μm. Dry after dull and dull, can withstand temperature 800 ℃, dry after the excellent conductivity.